metal injection molding and injection process
metal injection molding and injection process
metal injection molding production success depends on the accurate uniform control of the products, to ensure the dimens...
MIM sintering problem
MIM sintering problem
Sintering problem caused by one of the most important direct consequence is to make the product size change and affect t...
main cause of deformation of carbide sintered MIM
main cause of deformation of carbide sintered MIM
MIM of cemented carbide sintering deformation include: the main reasons for forming billet density is uneven
MIM carbide skimmed billet
MIM carbide skimmed billet
MIM carbide skim billet usually has about 60% of the relative density, relative density of the final product will reach ...
the MIM iron base alloy
the MIM iron base alloy
MIM iron base alloy is refers to the use of the preparation of metal injection molding for iron base (iron content is in...
316l stainless steel powder system
316l stainless steel powder system
316l stainless steel powder alloy powder system, the original system of alloy powder is a kind of uniform system of a si...
the performance of the MIM316L stainless steel
the performance of the MIM316L stainless steel
MIM316L stainless steel performance depends largely on densification degree of high and low, and the degree of densifica...
metal injection molding of stainless steel
metal injection molding of stainless steel
Now the most widely used metal injection molding of stainless steel 316 l stainless steel and 17 - PH stainless steel, 3...
the sintering of metal injection molding
the sintering of metal injection molding
Metal injection molding of sintering and general powder metallurgy sintering process is similar, but the metal injection...
metal injection molding billet
metal injection molding billet
After injection of billet in the binder is removal, sintering is a necessary step, sintering densification is usually ap...
A common problem of degreasing
A common problem of degreasing
Skim the carbon content is a common problem in the control, skim the existence of residual carbon is likely to cemented ...
crack
crack
Crack is easy to produce the green thickness changed a lot in area, thinner area binder removal could easily
skim the generation of crack
skim the generation of crack
Skim cracks may also be due to feed loading capacity is too low, as degreasing, binder is melting, the powder particles ...
the most common defects
the most common defects
Crack and deformation is one of the most common defects, degreasing degreasing rate must be controlled, and avoid the ge...
the MIM deviation problem in technology
the MIM deviation problem in technology
MIM technology has a shape change itself, but such change is predictable and usually is isotropic.And only commonly occu...
the goal of degreasing
the goal of degreasing
Skim goal is without defect and deformation of degreasing time as far as possible, and to ensure that the chemical compo...
skim temperature
skim temperature
Is important for solvent degreasing degreasing temperature, in order to not appear in the process of solvent degreasing ...
solvent degreasing model
solvent degreasing model
Macro performance solvent degreasing process is a solvent by outgoing gradually dissolve in briquette binder and purpose...
solvent degreasing
solvent degreasing
Solvent degreasing is solvent searches into the body, will be the binder ware into soluble dissolve out the process of s...
thermal degreasing in the final stages
thermal degreasing in the final stages
Binder removal is completed, through a period of up to another period of presintering, the degreasing process is complet...