MIM Watch Parts Gallery

MIM technology is widely used in watch parts production, no matter internal function parts or external watch case and strap. ZCMIM provide high precision watch case and strap with excellent strength properties. Further post-operations as PVD costing, polishing, grinding will be used to improve surface appearance.

MIM Watch Case

Material: Stainless steel 316L

Size: 37.84mm×42.04mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 37.81mm×41.89mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 39.64mm×52.86mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 40.67mm×48.45mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 46.14mm diameter

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, Polishing.

Material: Stainless steel 316L

Size:  44.79mm×56.00mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

ZCMIM projects

Start Your MIM Project Now


ZCMIM provide professional technology and experience team.

We are you reliable partner for every MIM project.

MIM Watch Strap

Material: Stainless steel 316L

Size: 23.7mm×40.15mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 316L

Size: 25.41mm×49.36mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 21.35mm×37.91mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 21.35mm×37.91mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

MIM Watch Assemble Parts

Material: Stainless steel 316L

Size: 26.53mm×7.45mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, Polishing.

Material: Stainless steel 316L

Size: 19.46mm×10.64mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, Polishing.

Material: Stainless steel 316L

Size: 9.3mm×32.0mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 25.25mm×29.4mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 316L

Size: 6.9mm×10.2mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 316L

Size: 9.57mm×67.21mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 22.35mm×42.79mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 13.8mm×15.9mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.