MIM Industrial Parts Gallery

MIM as the most cost-effective manufacturing way has widely application for industrial parts production. Our company has cooperated with thousands of  partners for their special projects.  ZCMIM main productions are micro-gears, drone metal parts, machinery components, and finally special design parts of pepper spray.

MIM Micro Gear

Material: Stainless steel 316L

Size: 8.01mm×12.15mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, Polishing.

Material: Stainless steel 304

Size:

Density: ≥7.8g/cm³

Properties: Tensile strength ≥ 500 MPa,

Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 304

Size: 19.73mm diameter

Density: ≥7.8g/cm³

Properties: Tensile strength ≥ 500 MPa,

Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 316L

Size: 28.00mm diameter

Density: ≥7.8g/cm³

Properties: Tensile strength ≥ 510 MPa,

Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

MIM Drone Part

Material: Stainless steel 316L

Size: 63.54mm in whole

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, Polishing.

Material: Stainless steel 316L

Size: 13.84mm≥12.9mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, Polishing.

Material: Stainless steel 304

Size: 16.22mm diameter, 3.5mm thickness

Density: ≥7.8g/cm³

Properties: Tensile strength ≥ 500 MPa,

Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

ZCMIM projects

Start Your MIM Project Now


ZCMIM provide professional technology and experience team.

We are you reliable partner for every MIM project.

MIM Pepper Spray Parts

Material: Stainless steel 316L

Size: 30.74mm×59.25mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 34.4mm×24.27mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 7.03mm×38.8mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, Polishing.

Material: Stainless steel 316L

Size: 26.14mm×19.76mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, Polishing.

MIM Machinery Component

Material: Stainless steel 316L

Size: 6.84mm×53.04mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 316L

Size: 3.91mm×49.55mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 316L

Size: 7.98mm×58.26mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 316L

Size: 8.47mm×7.98mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 316L

Size: 20.17mm×48.86mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding, PVD coating.

Material: Stainless steel 316L

Size: 18.4mm×28.56mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 316L

Size: 16.84mm×29.58mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.

Material: Stainless steel 316L

Size: 14.05mm×13.48mm

Density: ≥7.8g/cm³

Properties: Tensile strength of 510 MPa,

Yield strength≥180 MPa, Hardness of 120HV10.

Manufacturing process: Metal injection molding,

Magnetic grinding.